The Effect of Thickness of ZnO Thin Films on Hydrophobic Self-Cleaning Properties

Glass coating can be conducted by using ZnO-photocatalyst based semiconductor material since it is preeminent in decomposing organics compound and dangerous bacteria which often contaminates the environment. If there are dirt containing organics compound on the glass, the ZnO photocatalyst coat can be applied as self-cleaning, usually called self-cleaning glass. It depends on the coating thickness which can be controlled by setting the speed of spin coating. In this research, the various rotating speeds of spin coating were conducted at 2000 rpm, 3000 rpm, and 4000 rpm to control the thickness. The raw materials used in this research were Zn(CH₃COOH)₂.2H₂O (PA 99,5%), Ethylene glycol, Diethanolamine (PA 99%), Isopropanol Alkohol, Glycerol, and Ashton. Synthesis methods used were sol-gel prior to spin coating technic were applied. The results of the film were characterized by using SEM, XRD, and UV-Spectrophotometer. The crystal structure was analyzed by using Highscore plus and GSAS software, the size crystal was calculated by using Scherrer equation, a contact angle with ImageJ software. It was shown that ZnO thin film had been successfully synthesized with the crystal size around 21 nm up to 26 nm. The absorption value is higher due to the increasing of coat thickness with bandgap ± 3.2 eV. The test result of hydrophobic and hydrophilic characteristics show that all samples of ZnO thin film with the thickness ± 1.050 μm, ± 0.450 μm, ± 0.250 μm can be applied as self-cleaning glass. The best result was gained with the thickness of thin film ± 1.050 μm.