Abstract
Using a new electrolyte composition, which is stable against oxidation up to 5 V, the full electrochemical deintercalation of lithium from the spinel 
is studied. The origin of two new reversible oxidation‐reduction peaks near 4.5 and 4.9 V are examined. The capacity associated with these peaks depends on both the nominal composition 
in 
and the synthesis conditions (annealing temperatures and cooling rates), and thereby can be used as an indicator for electrochemically optimized 
powders. We present evidence that these peaks are related to local structural defects. Thermogravimetric measurements (TGA) on 
powders show a reversible loss of oxygen that can reach 5% at 1000°C. We find that some of this weight loss is associated with the conversion of cubic 
to a new tetragonal spinel phase and then to the decomposition of this phase into the orthorhombic 
phase plus other products. This new tetragonal 
spinel is prepared as a single phase, and its electrochemical properties are reported.